Available in stock
CSP is a patented 100% solid silicone modified polyurea. The silicone modification increases chemical resistance, lowers water absorption, improves UV resistance and has higher HDT. The CSP also meets the NSF-61 requirement for potable water.
US Patent #: 9,714,363
ChemSkin™ Polyurea (CSP) does not contain VOCs. Application temperature ranges from 40°F – 100°F. Functional operation temperature ranges from -40° to 250°F. CSP may be applied by a standard 2-component, high pressure spray machine. Substrate surfaces must be clean, dry and free of contaminates and dust. Substrates must be free of loose rust, paint, moisture, dirt oils, etc. If application surface exhibits extensive corrosion, spalling and/or weak deteriorating substrate, normal forms of media or shot blasting is recommended to create a secure surface preparation. For conditions which may only require liquid washing and cleaning with detergents, acids, bio-enzymes, etc. or conditions involving processes of scrubbing, rinsing and drying, the finish surface must not retain any residual cleaner unless specified by Superskinsystems, Inc. Concrete must be fully cured and should be prepared with shot blasting, diamond grinding or machine sanding depending on the severity of the concrete surface condition. Similar proper preparation must be performed for metal surfaces. Primers are recommended for proper preparation. Always power clean using mild detergent prior to sanding, etc. Spray coverage at 16 mils is 100 sq. ft./ mixed gallon.
| REGULAR | FLEXIBLE | SUPER-FLEX | ||
| Tensile Strength | ASTM D412 | 3750 psi | 2500 psi | 2200 psi |
| Elongation | ASTM D412 | 350% | 450% | 500% |
| Water absorption (24hr) | ASTM D570 | 0.25% | 0.25% | 0.25% |
| Moisture Vapor Transmission | ASTM E96 | 0.24 perms | 0.24 perms | 0.24 perms |
| Hardness | ASTM D785 | 60-75D | 80-75A | 70-75A |
| Abrasion -TaberCS17 | ASTM D4060 | <30 mg/1k cycles | <30 mg/1k cycles | <30 mg/1k cycles |
| Tear Strength | ASTM D624 | 690 lbs/ lin. in. | 500 lbs/ lin. in. | 300 lbs/ lin. in. |
| Gel Time | Time | 5-15 sec | 5-15 sec | 5-15 sec |
| Mix Ratio | PBV | 1:1 | 1:1 | 1:1 |
| Hose Heat | 160F | 160F | 160F | |
| Primary Heat | 160F | 160F | 160F | |
| Gun Pressure Minimum | 2000 PSI | 2000 PSI | 2000 PSI |
| Concrete- No Primer | >300 psi | Cohesive failure; excellent bonding |
| Steel- No Primer | >1000 psi | Excellent bonding |
| Composite Lamination | >1000 psi | Saturated; excellent bonding |
This technical data information is accurate to the best of our knowledge. SuperSkinSystems™ Inc. makes no warranty, expressed or implied within the materials on this website, its use or with its any application. SuperSkinSystems™ Inc. shall not be liable for material or application related injuries, material non-conformance, application failures or any consequential damage by the use of this product.